Product Description
Intense, saturated, clean, magenta. For high-quality kiln work, the flatter double-rolled glass minimizes bubble entrapment. Standard thickness is 3mm.
Bullseye Fuchsia Striker Transparent Bullseye White Opal is a lead-bearing glass that may react with glass that contains Sulfur/ Selenium bearing glass. The Standard thickness is 3 mm. 90 COE.
Striker glass: Glass matures to this color upon firing. The main image shows a sheet of the glass in strong light after firing. In the additional images you'll see a comparison swatch of the unfired glass color (top) and the glass after firing to a full fuse (bottom). Swatch image is about 1 inch wide.
Gold-bearing pink, purple, and coral transparents typically require a 2-hour hold at 1200°F–1225°F to fully develop color. Because this change occurs during the first firing and can’t be corrected later, testing is recommended.
Due to the many variables in production, each melt is unique and can be especially sensitive during firing. To support consistent results, Bullseye developed a “Gold Hold” best-to-test list highlighting colors that may under-develop in hotter-than-average kilns. See PDF for details. Results may vary.
Photo above is a general representation of glass colors. Colors may vary. Sizes are approximate.
Gold Hold